Latp Lithium Aluminum Titanium Phosphate Solid State Battery Electrolyte Sheet

• Separator Type: /
• Negative Materials: /
• Electrolyte: /
• Cathode Materials: /
• MOQ: 1 Bag
• Theoretical Density: 2.94G/Cm3
• Model NO.: TOB-LATP-E01
• Thickness: 260±10μm
• Diameter: 12±0.1mm
• Transport Package: Wooden Box
• Trademark: TOB
• Origin: China
• Production Capacity: 1000sets/Year

Product Description

LATP Lithium Aluminum Titanium Phosphate Solid State Battery Electrolyte Sheet

LATP solid state battery electrolyte has received extensive attention because of its excellent chemical and thermodynamic stability, extremely low raw material cost and preparation cost. It is a nano-solid electrolyte material that can be used for the preparation of all-solid-state lithium-ion batteries.

 

Model: TOB-LATP-E01

Conductivity: 2*10-4S/cm

 

Optional specifications:

1. Square 60*60mm

2. Single piece packaging with diameter of 12mm*260μm

3. Other sizes can be customized

 

Product name	Lithium Aluminum Titanium Phosphate Solid State Battery Electrolyte Sheet
Specification	Round sheet, diameter 12mm, thickness 260μm
Theoretical density	2.94g/cm^3
Chemical formula	Li1.3Al0.3Ti1.7P3O12
Shelf life	1 year
Items	Qualification standards	Unit	Detection method
Thickness	260±10	μm	Micrometer
Diameter	12±0.1	mm	Vernier caliper
Appearance	White, uniform color	/	Visual inspection
Main crystal phase	Consistent with the characteristic peak of PDF#35-0754	/	XRD
Ceramic sample ion conductivity@25ºC	≥0.45	mS/cm	AC impedance method
Flexural strength	≥130	MPa	Three-point bending resistance
Density	≥2.793	g/cm^3	Drainage method
Densification	≥95	%	Density/theoretical density*100%
Micromorphology	Magnification 20000, no more than 3 holes	/	SEM